Hardfacing by welding is the most economic way to enhance the life of the components which are exposed to high abrasion environment. Chromium rich electrodes are widely used due to their low cost. It is planned to study the effect of carbon and chromium over a wide range, on the resultant microstructure as well as wear behavior of the deposited layers, of the bottom plate of concrete mixer used in ready mix concrete plant.Six types of iron-based hardfacing electrodes with a wide range of C (0.6-5% by wt.) and Cr (3.5-35% by wt.) were selected to deposit, by the manual metal arc welding process on the mild steel plate of concrete mixer. The abrasive wear responses, hardness and the microstructures were compared with that of mild steel.Abrasion tests were carried out in a sliding wear abrasion test machine. surface analysis were made using SEM-EDAX, XRD Analysis.Field test was performed, by hardfacing on the actual size mild steel plate.The extent of improvement in wear performance of mild steel due to all hardfacing alloys is quite appreciable as compared to mild steel. Further the life of hardfaced plate was enhanced by 3.11 times compared to mild steel plate resulting net cost

Director / Principal (B.M.S. College of Engg.INDIA); Young Scientist & Best Engg. College Teacher Awardee; PhD: I.I.T. Roorkee,INDIA; Supervised numerous UG & PG Research Projects; Publications:71:International Referred Journals & Conferences; Filed 04 Patents; Supervising PhD Dissertations; Teaching & Research Experience 14 Years